LiVPO4F电子结构及电化学性质的第一性原理研究

唐鑫;钟胜奎;吕海峰

【期刊名称】《无机化学学报》 【年(卷),期】2011(27)6

【摘 要】Using the density-functional theory (DFT) combined with the projector augumented wave (PAW)method, we have investigated the crystal structure, electronic structure and electrochemical property of LiVPO4F.The change of structural parameters after the release of Li atom is obtained. Analysis of the density of states (DOS) show that V atom is ionized and its valence varies from +3 to +4 in the process of discharge. Also, the electron transfer between P and O atoms does not occur and the 3d-space structure of (PO4)3+ keep changeless approximatively. The band gap of LiVPO4F is 1.63 eV, which means that it has good conductivity and the electron transfer is facilitated in discharge. Our results also indicate that LiVPO4F is a ferromagnetic phase and its ferromagnetic moment is 2μB, but VPO4F is a anti-ferromagnetic phase. Furthermore, it was found that the average intercalation voltage of LiVPO4F has the value of 4.0 eV.%采用密度泛函理论(DFT)结合投影缀加波(PAW)方法,对LiVPO4的晶体结构,电子结构和电化学属性进行了研究.从理论上获得了脱Li前后具体的晶格参数的变化.通过对其态密度的计算,发现在放电过程中.V在化合物中呈现离子态.发生+3/+4价态的转变,电子转移主要发生在V原子上;而P原子的状态比较稳定,并不发生大的电子的转移,磷酸根的空间结构也变化不大.同时HVPO4F的禁带宽度仅为1.63 eV,说

明其在一定情况下具有良好的导电性,有利于放电过程中电子的输运.IaVPO4F是铁磁相,磁矩为2μB,而VPO4F为反铁磁相.此外,通过计算获得了HVPO4F的平均嵌锂电压为4.0 eV.

【总页数】6页(P1065-1070) 【作 者】唐鑫;钟胜奎;吕海峰

【作者单位】有色金属及材料加工新技术教育部重点实验室,桂林理工大学,桂林,541004;桂林理工大学材料科学与工程学院,桂林,541004;桂林理工大学化学与生物工程学院,桂林,541004;中国科学院计算机网络信息中心超级计算中心,北京,100080 【正文语种】中 文

【中图分类】O611.2;O641.13 【相关文献】

1.掺杂CeO2光学性质和电子结构的第一性原理研究 [J], 李旭;申家欣;郑浩然 2.缺陷情况下ZnO电子结构的第一性原理研究 [J], 范雅文;冯金娇;赵辉

3.不同氧化锆相的稳定性及电子结构的第一性原理研究 [J], 温新竹;刘明真;彭玉颜 4.外力对三元哈斯勒半金属ZrIrSb电子结构和光学性质影响的第一性原理研究 [J], 韦俊红;孔慧君;刘潇;张敏平

5.外力对三元哈斯勒半金属ZrIrSb电子结构和光学性质影响的第一性原理研究 [J], 韦俊红;孔慧君;刘潇;张敏平

因版权原因，仅展示原文概要，查看原文内容请购买